Pemulihan kompaun sulfur daripada karbon teraktif penuh dengan hidrogen sulfida menggunakan bahan kimia yang berbeza telah disiasat. Bahan kimia yang telah dikaji adalah hidrogen peroksida (H2O2), natrium hidroksida (NaOH) dan dietanolamina (DEA). Bahan kimia yang terbaik telah dipilih untuk menyiasat lebih lanjut kesan daripada kepekatan, masa dan suhu terhadap jumlah pemulihan sulfur. Pengoptimuman kajian telah dilakukan dengan bahan kimia yang dipilih. Dari hasil kajian, hanya H2O2 dapat memulihkan sebatian sulfur daripada rawatan manakala penggunaan NaOH dan DEA gagal mendapatkan apa-apa produknya maka H2O2 telah dipilih untuk kajian selanjutnya. Pengoptimuman pemulihan sulfur dikenal pasti pada 40 v / v% daripada H2O2, masa pengoksidaan 24 jam dan pada 70 0C. Di bawah keadaan ini, pemulihan sulfur adalah 49.62% berat sulfur. Analisis keputusan ujikaji menunjukkan bahawa pemulihan sulfur dipengaruhi oleh kepekatan kerana jumlah molekul oksidan masa ini, diperolehi dengan masa pengoksidaan dengan H2O2 yang disebabkan oleh jumlah interaksi oleh molekul dan dipengaruhi oleh suhu kerana lebihan haba.
_______________________________________________________________________________________________________
The recovery of sulfur compound from activated carbon exhausted with hydrogen sulfide using different chemicals has been investigated. The chemicals that has been studied are hydrogen peroxide (H2O2), sodium hydroxide (NaOH) and diethanolamine (DEA). The best from the chemicals used has been chosen to further investigate the effect of concentration, time and temperature towards the amount of sulfur recovery. Optimization study was done with the selected chemical. From the result, only H2O2 is able to recover the sulfur compound from the treatment while the usage of NaOH and DEA failed to recover any of its product thus H2O2 was selected to further studied. The optimal sulfur recovery conditions were determined as 40 v/v % of H2O2, oxidation time of 24 hours at 70 0C. Under these condition, the sulfur recovery was 49.62 wt% of sulfur. Analysis of the experimental results shows that the sulfur recovery is affected by concentration due to the amount of oxidant molecules present, effected by the oxidation time with the H2O2 due to the amount of interaction by the molecules and affected by temperature due to the external heat available.