Kerja-kerja ini memberi tumpuan kepada sintesis, pencirian dan aktiviti fotokatalitik
katalis komposit (TiO2/Fe2O3) dalam penguraian fluoranthene (FLT) dan pyrene (PYR)
dengan menggunakan proses fotokatalisis heterogen. Sampel telah disintesis oleh kaedah
yang murah dan bersifat alam semula jadi sol-gel dan dicirikan dengan menggunakan
teknik seperti Penyebaran X-Ray (XRD), Mikroskopi Mengimbas X-Ray - Tenaga
Diskriminasi X-Ray (SEM-EDX), Penyebaran UV-Vis Refleksi Spektrum (UV-Vis
DRS) dan Brunauer-Emmett-Teller (BET). Air hujan sintetik digunakan di bawah
keadaan eksperimen pH dan kepekatan (TiO2/Fe2O3) yang berbeza-beza. Untuk
memaksimumkan kecekapan proses, kaedah permukaan respon (RSM) digunakan
dengan mempertimbangkan dua pembolehubah bebas pH dan kepekatan (TiO2/Fe2O3).
Dalam kajian ini, kepekatan bahan pencemar sentiasa berubah sepanjang proses rawatan.
Titania yang telah dicampur ferum menunjukkan bahawa ia mempunyai kawasan
permukaan (80.9 m2/g), jurang sempit (1.6 eV) dan dapat menyerap panjang gelombang
di rantau yang kelihatan sehingga (> 400 nm). Penyingkiran peratusan yang tertinggi
diperoleh daripada eksperimen (sebenar) untuk FLT dan PYR selepas 30 minit masa
penyingkiran adalah 75 % dan 87 %, manakala selepas 60 minit masa penyingkiran,
peratusan penyingkiran untuk FLT dan PYR adalah 97 % dan 92 %, berlaku dalam
keadaan pH=5 dan sekurang-kurangnya pada dos 0.25 g/L (TiO2/Fe2O3). Degradasi
pencemar yang diperolehi dalam kajian ini mengesahkan penggunaan cahaya matahari
semulajadi yang mungkin sebagai sumber UV untuk proses fotokatalisis.
_______________________________________________________________________________________________________
The present work focuses on the synthesis, characterization and photocatalytic activity
of a composite catalyst (TiO2/Fe2O3) in degradation of fluoranthene (FLT) and pyrene
(PYR) using heterogeneous photocatalysis process. The samples were synthesized by the
inexpensive and environmentally sol–gel method and characterized by using techniques
such as X-RayDiffraction (XRD), Scanning Electron Microscopy-Energy Dispersive XRay
(SEM-EDX), UV–Vis Diffuse Reflectance Spectra (UV-Vis DRS) and Brunauer-
Emmett-Teller (BET). Synthetic rainwater was used under different experimental
conditions of pH and concentration of the (TiO2/Fe2O3). In order to maximize the process
efficiency, response surface methodology (RSM) was used by considering two
independent variables of pH and (TiO2/Fe2O3) concentration. In this study, the
concentration of the pollutants were kept constant throughout the treatment process. The
result of characterization showed that doped titania has high surface area (80.9 m2/g),
narrow band gap (1.6 eV) and able to absorb wavelength in the visible region up to (>400
nm). The highest percentage of removal obtained from the experimental run (actual) for
FLT and PYR 30 minutes after treatment are 75% and 87%, respectively, while for after
60 minutes of treatment for FLT and PYR are 97% and 92% respectively, occurs at
optimum condition of pH=5 and minimum dosage of (TiO2/Fe2O3) of 0.25 g/L. The
degradation of pollutants obtained in this study confirmed the feasible use of natural
sunlight as the UV source for the photocatalysis process to take place.
Treatment of synthetic rainwater using composite catalyst-(tio2fe2o3) by photocatalysis process / Nur Afiqah Abdullah