Repetitive magnetization of nanomaterials on influencing magnetophoresis at low field gradient

Repetitive magnetization of nanomaterials on influencing magnetophoresis at low field gradient / Roslia Rosli
Kajian ini adalah untuk mengkaji kesan pemagnetan berulang-ulang pada magnetophoresis. Selain itu, nanopartikel oksida besi magnet (MIONPs) yang dibeli dari OceanNano juga digunakan sebagai sampel untuk membandingkan keputusan dengan nanopartikel oksida besi magnet (MIONPs) yang disintesis. Saiz pengedaran hidrodinamik nanopartikel ditentukan melalui pengukuran keamatan penggantungan nanopartikel oksida besi magnet (MIONPs) dengan menggunakan penyerakan cahaya dinamik (DLS) untuk mengkaji saiz nanopartikel oksida besi magnet (MIONPs) sebelum dan selepas setiap magnetophoresis di bidang kecerunan rendah. Selain itu, UV-Vis spektrofotometer telah digunakan untuk menyiasat tingkah laku magnetophoresis nanopartikel oksida besi magnet (MIONPs). Kelakuan magnetophoresis diulang sebanyak lima kali dengan menggunakan sampel yang sama untuk mengenal pasti profil pemisahan nanopartikel oksida besi magnet (MIOPs) bagi setiap pengulangan. Berdasarkan keputusan eksperimen, pemagnetan yang berulang-ulang memberi kesan ke atas masa pemisahan di kecerunan medan rendah. Kedua-dua sampel memberi kesan tingkah laku magnetophoresis yang sama. Saiz nanopartikel oksida besi magnet MIONPs meningkat dengan pemagnetan berulang yang semakin meningkat kerana pengagregatan bidang dan menyebabkan pemisahan yang lebih cepat. _______________________________________________________________________________________________________ This study is to study repetitive magnetization effects on magnetophoresis. Apart from that, MIONPs purchased from OceanNano are also used as sample to compare the result with the synthesized MIONPs. Hydrodynamic size distribution of nanoparticles was determined through intensity measurement of the MIONPs suspension using dynamic light scattering (DLS) to study the size of MIONPs before and after each magnetophoresis at low field gradient. Moreover, UV-Vis spectrophotometer was utilized to investigate the magnetophoresis behavior of MIONPs. The magnetophoresis behavior experiment is repeated for five times using same sample in order to identify the separation profile of MIOPs for each repetition. Based on the experiment, the repetitive magnetization gives effect on separation times at low field gradient. Both sample give same effect of magnetophoresis behavior. The size of MIONPs is increase with the increasing repeated magnetization due to field-induced aggregation which resulting faster separation times.
Contributor(s):
Roslia Rosli - Author
Primary Item Type:
Final Year Project
Identifiers:
Accession Number : 875005677
Language:
English
Subject Keywords:
magnetization; magnetophoresis; Hydrodynamic
First presented to the public:
5/1/2015
Original Publication Date:
7/29/2020
Previously Published By:
Universiti Sains Malaysia
Place Of Publication:
School of Chemical Engineering
Citation:
Extents:
Number of Pages - 46
License Grantor / Date Granted:
  / ( View License )
Date Deposited
2020-07-29 10:07:58.217
Date Last Updated
2020-07-29 10:08:59.557
Submitter:
Mohd Jasnizam Mohd Salleh

All Versions

Thumbnail Name Version Created Date
Repetitive magnetization of nanomaterials on influencing magnetophoresis at low field gradient1 2020-07-29 10:07:58.217
Engineering Library USM @ 2017